Oxford Zircore NANO Zirconia-Reinforced Core Build-up Material

Introducing Oxford Zircore NANO Dual Cure, Zirconia-Reinforced Core Build-up Material

New Zirconia-Reinforced Core Material that is Strong, Reliable and Economical. Oxford Zircore NANO is a dual cure, resin core build-up material reinforced with zirconia nano particles for outstanding physical properties without affecting the material’s ability to stack and flow. Oxford Zircore NANO is supplied in 5ml automix syringes to facilitate easy placement of the material onto the tooth’s surface or into a post space when used as a post cement. The product is available in tooth colored and contrast shades.

Features and Benefits: Feature:

Benefit:

•— Reinforced with Zirconia Nano Particles

•— Very high flexural and compressive strengths •— “Cuts like dentin” •— High strength in both light and self cure mode •— Enhances the radiopacity when used as a cement

•— Dual Cure

•— Greater versatility •— Saves time

•— Reliable

•— Does not lose significant elastic modulus when used in the self cure mode

•— Versatile

•— Can be used as a core material or a post cement

•— Thixotropic, yet Flowable

•— Easy to build and sculpt cores •— Good flow for usage as a cement

•— Automix Syringe Dispensing

•— Void free mixing •— Less threatening to patients •— Greater visibility in the oral cavity

•— Value Priced

•— Economical — Saves money

Oxford Scientific

OxfordZircoreNANOSellSheet_v2_9_10:Layout 1

11/8/10

7:08 PM

Page 2

Oxford Zircore NANO Zirconia-Reinforced Core Build-up Material

Oxford Zircore NANO has Superior Physical Properties.

Oxford Zircore NANO is Strong.

Oxford Zircore NANO — reliable in both Light and Self Cure Modes. Elastic Modulus of Leading Core Materials after Light Cure (LC) and Self Curing (SC) Modes*

Compressive Strength of Leading Core Materials in MPa*

350

325

317

10000

305

300

8500 LC 4300 SC

7800 LC 5200 SC

7600 LC 5100 SC

8000

250 195

200

MPa

8000 LC 7200 SC

6000

MPa M

150

4000

100 2000

50 0

Oxford Zircore NANO

Rebilda

LuxaCore Automix Dual

(VOCO)

LuxaCore Automix Dual Z

0

Oxford Zircore NANO

Rebilda (VOCO)

LuxaCore Automix Dual

LuxaCore Automix Dual Z

(Zenith DMG)

(Zenith DMG)

*Data available upon request.

Physical Data

•— Light Cure Time:

20 Seconds

•— Elastic Modulus (LC):

8000 MPa

•— Depth of Cure:

2.5 – 5mm (according to darkness of shade)

•— Elastic Modulus (SC):

7200 MPa

•— Self Cure Time:

3 Minutes, 30 Seconds

•— Compressive Strength:

325 MPa

•— Barcol Hardness:

70

•— Diametral Tensile Strength:

44 MPa

Ordering Information

Oxford Zircore NANO Dual Cure, Zirconia-Reinforced Core Build-up Material 2 — 5 ml - 9 gm syringes | 10 mixing tips Part Number

Description

•— FE-001

Oxford Zircore NANO A2

•— FE-002

Oxford Zircore NANO A3

•— FE-003

Oxford Zircore NANO White

•— FE-004

Oxford Zircore NANO Blue

Imported Exclusively to North America by

Finnigan Enterprises, LLC

|

Meriden CT., 06450

888-686-1950 | 203-686-1464 | www.oxfordscientificdental.com

fax: 203-686-0188

© 2010 Copyright Finnigan Enterprises, LLC. All Rights Reserved.

Oxford Scientific M a d e i n G e r m a n y b y F i r s t S c i e n t i f i c D e n t a l M a t e r i a l s G m b H.