Selective Cation Exchange in the Core Region of ... - ACS Publications


Selective Cation Exchange in the Core Region of...

0 downloads 80 Views 1MB Size

Subscriber access provided by CMU Libraries - http://library.cmich.edu

Communication

Selective Cation Exchange in the Core Region of Cu2-xSe/Cu2-xS Core/Shell Nanocrystals Karol Miszta, Graziella Gariano, Rosaria Brescia, Sergio Marras, Francesco De Donato, Sandeep Ghosh, Luca De Trizio, and Liberato Manna J. Am. Chem. Soc., Just Accepted Manuscript • DOI: 10.1021/jacs.5b06379 • Publication Date (Web): 11 Sep 2015 Downloaded from http://pubs.acs.org on September 18, 2015

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Journal of the American Chemical Society is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 5

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Journal of the American Chemical Society

Selective Cation Exchange in the Core Region of Cu2-xSe/Cu2xS Core/Shell Nanocrystals Karol Miszta,† Graziella Gariano,† Rosaria Brescia,† Sergio Marras, Francesco De Donato, Sandeep Ghosh, Luca De Trizio,* and Liberato Manna* Department of Nanochemistry, Istituto Italiano di Tecnologia (IIT), via Morego, 30, 16163 Genova, Italy KEYWORDS: cation exchange, nano heterostructures, metal chalcogenides

ABSTRACT: We studied cation exchange (CE) in core/shell Cu2+ 2+ xSe/Cu2-xS nanorods with two cations, Ag and Hg , which are known to induce rapid exchange within metal chalcogenide nanocrystals at room temperature. At the initial stage of the reaction, the guest ions diffused through the Cu2-xS shell and reached the Cu2-xSe core, replacing first Cu+ ions within the latter region. These experiments prove that CE in copper chalcogenide nanocrystals are facilitated by the high diffusivity of guest cations in the lattice, such that they can probe the whole host structure and identify the preferred regions where to initiate the exchange. In both cases, CE is thermodynamically driven as it aims for the formation of the chalcogen phase characterized by the lower solubility under the specific reaction conditions.

Colloidal inorganic nanocrystals (NCs) are a testing ground for chemical and structural nanoscale transformations. Cation exchange (CE), for example, has been studied in ionic NCs also as a means to implement current synthesis techniques.1 An interesting aspect of CE applied to NCs is that its intermediate steps often consist of multidomain heterostructures. For example, partial CE performed on anisotropic NCs (i.e. nanorods, nanoplatelets, nanowires) can lead to heterostructures evidencing a replacement of cations only at the tips or in specific sections of the NCs.2 Similarly, isotropic NCs can evolve into Janus-like or to core/shell structures when partially exchanged.3 Especially the Janus-like architectures appear to indicate that there exist regions on the surface of NCs acting as preferential entry points for cations, where the exchange is initiated and from which it proceeds to the remaining volume of the NC, so that both the interfacial energy and the elastic strain between the two different phases are minimized.2b New insights into ion diffusion and CE reactions in NCs came from recent works on CE in CdSe NCs4 that demonstrated how Ag+ ions, once incorporated in the NCs, could easily probe the whole NC lattice, via interstitial diffusion. As soon as a critical concentration of Ag+ ions was reached, their mutual repulsion caused their segregation closer to the surface of the NCs, where the Ag+ ions could start replacing Cd2+ ions. This was also proven in a recent work by optically monitoring the same reaction with single NC resolution.5 Therefore, while in CE reactions in NCs there could be multiple entry points for ions (virtually the whole NC surface), the actual exchange, initiated by ions that have already diffused in the particles, can start from a region inside the NC that does not necessarily coincide

with the entry point(s). This should be especially true when the guest ions are fast diffusing in the host lattice, so that they can quickly probe the whole NC in the quest for regions where it would be energetically more favorable for them to engage in CE reactions. Ideal NC samples on which to probe these hypotheses are represented by copper chalcogenide NCs, as done in this work, since they are characterized by a large density of Cu vacancies that promote fast ion diffusion (through both interstitial and vacancy sites)6 facilitating CE with many different guest cations. These NCs can be easily fabricated, for example from the corresponding cadmium chalcogenide NCs (again by CE, see Supporting Information (SI) for details),2b-d,7 providing an ample set of samples, in terms of sizes, shapes and architectures, to start with. It is worth underlining that the Cu-chalcogenide NCs obtained through CE from Cdchalcogenide NCs are normally characterized by a slight copper deficiency, due to the ease of formation of Cu vacancies, and as a direct consequence they exhibit a localized surface plasmon resonance band (see Figure S1 in the SI).2h,7a As test cations, we chose Ag+ and Hg2+, as they have already been proven to induce CE in metal chalcogenides at room temperature conditions.2a,8 The different reactivities of the two cations were taken into account when choosing the appropriate feed ratios when performing CE reactions. When Cu+ cations in Cu2-xS nanorods (NRs) were partially replaced by Hg2+ ions, the NRs evolved into multidomain structures, similarly to what observed by other groups when exposing CdS NRs or Cu2S nanowires to Cu+ or Ag+ ions, respectively.2e,6,7b This is seen in the high angle annular dark field (HAADF) scanning transmission electron microscopy (STEM) images of Figure 1a,c, and in the compositional maps acquired via energy dispersive X-ray spectroscopy (EDS). In the Ag+ case, the NRs were converted into a mixture of rods with a segmented structure and rods with ternary composition (see Figure 1b and selected area electron diffraction (SAED) analyses in Figure S2 of the SI). In some of the partially exchanged NRs, a slightly Ag-rich shell was also visible. The two cations, despite having similar ionic radii (Ag+=1.0 Å and Hg2+=0.96 Å in tetrahedral coordination),9 seemed to behave differently: the Ag+ ions appeared to probe the entire NR volume, while the Hg2+ ions were mainly engaged in reactions that started at the tips of the rods. We then extended this reaction scheme to core/shell Cu2-xSe/Cu2-xS NRs. A comparison of HAADF-STEM and EDS analyses of the initial sample with those after partial exchange indicated a selective re-

ACS Paragon Plus Environment

Journal of the American Chemical Society

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

placement of Cu+ ions in the selenide core region (see Figure 2 and Figures S3,S4 in the SI).

Page 2 of 5

XRD patterns of the pristine Cu2-xSe/Cu2-xS NRs (Figure 3c) were dominated by the hexagonal Cu2S (high chalcocite) peaks, with other minor reflections ascribable to the metastable Cu2Se “chalcocite-like” phase, as previously reported by us.7a the XRD patterns of partially exchanged NRs in both cases evidenced instead the presence of high chalcocite Cu2S, together with a second majority phase that, in the case of Ag+treated NRs, could be indexed according to the orthorhombic Ag2Se (naummanite) phase (see Figure 3b), while for the Hg2+-treated rods it could not be indexed to any known bulk HgSe or to any alloyed HgSexS1-x phase.

Figure 1. CE in Cu2-xS NRs with Ag+ and Hg2+ ions. HAADFSTEM images of representative groups of (a) pristine, (b) Ag+ and (c) Hg2+ partially exchanged Cu2-xS NRs with the corresponding STEM-EDS elemental maps. Scale bars are 20 nm.

Figure 2. CE in Cu2-xSe/Cu2-xS NRs with Ag+ and Hg2+ ions. HAADF-STEM images of groups of (a) pristine, (b) Ag+ and (c) Hg2+ partially exchanged Cu2-xSe/Cu2-xS NRs with the corresponding STEM-EDS elemental maps. Scale bars are 20 nm.

These findings were supported by elemental analyses (via STEM-EDS), which yielded a Hg/Se ratio of ~1 and a Ag/Se ratio of ~2 for the Hg-treated and Ag-treated NRs, respectively (Table S1). High resolution TEM (HRTEM) images of partially exchanged Cu2-xSe/Cu2-xS NRs, with both Ag+ and Hg2+ ions, reported in Figure S5, confirmed the selective ion replacement in the core region and, importantly, showed a continuous shell, exhibiting no cracks, surrounding the cores.. The exposure of Cu2-xSe/Cu2-xS NRs to an higher amount of Ag+ or Hg2+ ions led to an almost complete replacement of Cu+ ions (see Figures S6, S7 and Table S1). The peculiarity of these results stands in the evidence that cation replacement in the Cu2-xSe core must be preceded, both for Ag+ and Hg2+ cations, by diffusion of cations through the Cu2-xS shell. The structural transformations of the core/shell Cu2-xSe/Cu2-xS NRs upon partial CE were monitored via X-ray diffraction (XRD). The

Figure 3. XRD patterns of (c) pristine, (b) Ag+ and (a) Hg2+ partially exchanged Cu2-xSe/Cu2-xS NRs, with bulk reflections of hexagonal Cu2S (high chalcocite, ICDD 98-016-6578) and orthorhombic Ag2Se (naumannite, ICDD 98-026-1822). Reflections of the Cu2Se “chalcocite like” phase are adapted from ref.7a. The Bragg peaks emerging after Hg2+ partial exchange correspond to the bulk reflections of hexagonal CdSe (cadmoselite, ICDD 96901-6057). In all samples, other minor peaks (labeled with *) can be assigned to a sub-stoichiometric tetragonal Cu116S64 phase (roxbyite, ICDD 96-901-5183), probably appearing due to slight oxidation of the NC films exposed to air during pattern acquisition.

By extending the search to other known phases, these peaks could be well matched with the hexagonal CdSe (cadmoselite) structure (Figure 3a). Since no traces of Cd were detected by elemental analysis, the formation of a ”cadmoselite like” hexagonal HgSe phase is likely due to the topotactic replacement of Cu+ ions with Hg2+ ions in the core region, with preservation of the hexagonal structure of the Se2- anion sublattice. Overall, XRD analyses corroborated the preservation of the Cu2S shell and, at the same time, the selective replacement of Cu+ ions in the core region with Ag+ or Hg2+ cations. By combining results from experiments on Cu2-xS and on core/shell Cu2-xSe/Cu2-xS NRs, we can state that the initial step in the CE reactions is represented by the diffusion of the guest cations (Ag+ and Hg2+) in the NCs, most likely from multiple entry locations. In the Cu2-xSe/Cu2-xS NRs, the guest ions, after having diffused through the Cu2-xS shell and probed the whole NC volume, selectively replaced Cu+ host ions within the Cu2-xSe

ACS Paragon Plus Environment

Page 3 of 5

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Journal of the American Chemical Society

core. If one considers bond dissociation energies, CE involving Cu2-xS or Cu2-xSe NCs should not occur, since stronger CuS or Cu-Se bonds are broken to form weaker M-S and M-Se (M=Ag, Hg) bonds (Table 1). However, the overall energy balance includes also solvation energies of the exchanging cations, which in most cases creates the actual driving force.1b As in these CE reactions no phosphine was used, but methanol was the only Lewis base promoting the exchange (see SI for details), the thermodynamic feasibility of CE can be tentatively rationalized by the trend in solubility product constants (KSP) of the materials involved1e (Table 1). It is known that a ionic solid with a relatively high KSP can spontaneously transform, trough CE, to another ionic solid with a lower KSP. As Ag2E and HgE (E=S, Se) are less soluble in polar solvents than the corresponding Cu2E solids, the former are thermodynamically favored. Moreover, metal selenides are generally characterized by lower KSP than their corresponding sulfides.10 Therefore, when both Cu2-xSe and Cu2-xS domains are exposed to an amount of guest cations that enables competition between the two, CE is more likely to occur in the metal selenide domain. Table 1. Bond Dissociation Energies (BDEs, expressed in kJ/mol) (from ref.11) and Solubility Product constants (KSP, at 25°C) of different metal chalcogenides (from refs.1e,12) Material

E=S BDE

E=Se KSP 6.3 * 10

-50

BDE

KSP

210.0±14.6

3 * 10-54

Ag2E

216.7±14.6

CdE

208.5 ± 20.9

1 * 10-28

127.6 ± 25.1

4 * 10-35

Cu2E

274.5±14.6

2.5 * 10-48

255.2±14.6

N.A.

HgE

217.3±22.2

6 * 10-53

144.3±30.1

4 * 10-59

Also, the Cu2-xSe core, compared to the Cu2-xS shell, has a stronger tendency to form Cu vacancies, as found by us in a previous work by exposing the rods to oxidizing agents:8c this led to the formation of hollow particles by coalescence of the Cu vacancies that had gathered in the Cu2-xSe core. Here, it is possible that a larger density of Cu vacancies in the core would additionally favor the diffusion of guest cations in such region. Our experiments show that in “simple” Cu2-xS rods, which lack such preferred region, the guest Hg2+ ions, after having likely probed the whole rod, found the outer surface layers and/or the rod tips as the most convenient regions where to initiate exchange. For Ag+, this preference was less marked, since also particles with ternary composition were found (see Figure 1b).4b These considerations may help elucidating how CE can proceed in NCs in which ions have high diffusivity: guest ions can diffuse in host NCs and target the preferred region where to initiate CE rather than necessarily replace original cations starting from the NCs surface, as commonly believed. This argument is supported by additional tests employing Au3+ ions as guests in core/shell Cu2-xSe/Cu2-xS NRs. Here too, partially exchanged samples evidenced a selective localization of Au ions in the core (see Figure S8). This was corroborated by STEM-EDS elemental analyses in which a Au/Se ratio of 0.7 was measured, suggesting the formation of a Au1xSe phase in the core region (Table S1). These experiments were then benchmarked against CE on CdSe/CdS nano-heterostructures. In cadmium chalcogenide structures, where the density of vacancies is considerably low-

er than in Cu-based ones, ion diffusion proceeds mostly interstially. When CdSe/CdS NRs were partially exchanged with Ag+ ions, no preferential exchange of the core was observed (see Figure S9). Instead, at the early stage of the CE process, Ag-containing domains started “decorating” the CdS outer layer, accompanied by the replacement of Cd2+ ions at the tips of the rods, producing heterostructures similar to the Ag2SCdS NRs reported in the literature.2a Also, in a previous work of ours, we studied CE involving CdSe/CdS octapod-shaped NCs with Cu+ ions, in conditions that are similar to those of this work:2c in that case too, the CE started at the extremities of the CdS pods and left the CdSe core unaltered. Furthermore, our data are in line with those of recent works in which it was shown that partial exchange of core/shell CdSe/CdS nanoplatelets and NRs with Cu+ ions resulted in a selective replacement of Cd2+ cations in the CdS shell.13 In the light of the data discussed on Cu2-xSe/Cu2-xS NRs so far, these results suggest that, in CdSe/CdS NRs, even if the thermodynamically preferred phases would be Cu2Se and Ag2Se (Table 1), the limited diffusivities of both the entering Cu+ or Ag+ cations and the exiting Cd2+ ions are mainly responsible for the preferential nucleation of the Cu2S or Ag2S phases at regions of the NCs close to their surface. We also ran control experiments starting from “inverted” core/shell Cu2-xS/Cu2-xSe NRs, prepared by complete Cu+ exchange on CdS/CdSe NRs (see SI).8c When partial exchange with Ag+ or Hg2+ ions was carried out on them, the replacement affected selectively the shell region (i.e., the Cu2-xSe phase), as shown in Figure 4 (see also Table S1). It is interesting to notice that, in CE reactions involving Hg2+ ions, there was a substantial anion inter-diffusion throughout the NRs (Figure 4b). This further proves that CE, affecting in this case mainly the shell region, represents only the final step of a series of events in which Hg2+ ions had previously probed extended regions inside the rods, in this case partially “dragging”, along their way, S2- and Se2- ions.

Figure 4. CE in “inverted” core/shell Cu2-xS/Cu2-xSe NRs, with Ag+ and Hg2+ ions. HAADF-STEM images of representative “inverted” NRs partially exchanged with (a) Ag+ or (b) Hg2+, along with the corresponding STEM-EDS elemental maps. The scale bars in the images are 20 nm.

In yet another control experiment, a mixture of Cu2-xS and Cu2-xSe NCs, prepared by standard direct synthesis protocols, and not via CE (see SI for details), was exposed either to Ag+ or to Hg2+ ions. Here too, the experiments were run with Ag/Cu or Hg/Cu feed ratios that were insufficient to achieve a complete replacement of the copper ions, in order to trigger competition between the two different types of NCs towards CE (see SI for experimental details). In analogy with the ex-

ACS Paragon Plus Environment

Journal of the American Chemical Society

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

periments discussed above, CE selectively affected the Cu2-xSe NCs rather than the Cu2-xS ones (see Figure 5). These experiments rule out any potential influence of the preparatory history of the copper chalcogenide NCs (i.e., whether they were synthesized directly or they were prepared instead by CE) on their reactivity towards the guest cations.

Figure 5. CE in a mixed population of Cu2-xS and Cu2-xSe NCs with Ag+ and Hg2+ ions. HAADF-STEM images of groups of copper sulfide and copper selenide NCs exposed to (a) Ag+ or (b) Hg2+ ions with the corresponding STEM-EDS elemental maps. The scale bar in each image is 20 nm.

In conclusion, we have shown that in partial CE involving core/shell Cu2-xSe/Cu2-xS NRs exposed to Ag+, Hg2+ and Au3+ ions, a selective replacement of the core cations occurred. This selective CE is made possible by the high ion diffusivity in copper chalcogenides as it allows guest cations to probe the whole structure and initiate the exchange in the core rather than in the shell. The overall process, on the other hand, is driven by thermodynamics factors which favor the formation of metal selenides over the corresponding sulfides in our reaction environment. Our hypotheses were supported by various control experiments. The ability to selectively transform the core in core/shell copper chalcogenide NCs offers an additional tool to tailor the topology and the chemical composition of colloidally synthesized nanoparticles.

ASSOCIATED CONTENT Supporting Information. Details on chemicals, syntheses, reactions, structural and compositional characterization. This material is available free of charge via the Internet at http://pubs.acs.org.

AUTHOR INFORMATION

Page 4 of 5

We acknowledge funding from the European Union under grant agreement n. 614897 (ERC Grant TRANS-NANO). We thank Andreas Riedinger for helpful discussion.

REFERENCES (1) a) Beberwyck, B. J.; Surendranath, Y.; Alivisatos, A. P. J. Phys. Chem. C 2013, 117, 19759; b) Rivest, J. B.; Jain, P. K. Chem. Soc. Rev. 2013, 42, 89; c) Buck, M. R.; Schaak, R. E. Angew. Chem. Int. Ed. 2013, 52, 6154; d) Gupta, S.; Kershaw, S. V.; Rogach, A. L. Adv.Mater. 2013, 25, 6923; e) Moon, G. D.; Ko, S.; Min, Y.; Zeng, J.; Xia, Y.; Jeong, U. Nano Today 2011, 6, 186. (2) a) Robinson, R. D.; Sadtler, B.; Demchenko, D. O.; Erdonmez, C. K.; Wang, L.-W.; Alivisatos, A. P. Science 2007, 317, 355; b) Sadtler, B.; Demchenko, D. O.; Zheng, H.; Hughes, S. M.; Merkle, M. G.; Dahmen, U.; Wang, L.-W.; Alivisatos, A. P. J. Am. Chem. Soc. 2009, 131, 5285; c) Miszta, K.; Dorfs, D.; Genovese, A.; Kim, M. R.; Manna, L. ACS Nano 2011, 5, 7176; d) Luther, J. M.; Zheng, H.; Sadtler, B.; Alivisatos, A. P. J. Am. Chem. Soc. 2009, 131, 16851; e) Tan, C.-S.; Hsiao, C.-H.; Wang, S.-C.; Liu, P.-H.; Lu, M.-Y.; Huang, M. H.; Ouyang, H.; Chen, L.-J. ACS Nano 2014, 8, 9422; f) Jeong, S.; Han, J. H.; Jang, J.t.; Seo, J.-w.; Kim, J.-G.; Cheon, J. J. Am. Chem. Soc. 2011, 133, 14500; g) Casavola, M.; van Huis, M. A.; Bals, S.; Lambert, K.; Hens, Z.; Vanmaekelbergh, D. Chem. Mater. 2012, 24, 294; h) Zhang, D.; Wong, A. B.; Yu, Y.; Brittman, S.; Sun, J.; Fu, A.; Beberwyck, B.; Alivisatos, A. P.; Yang, P. J. Am. Chem. Soc. 2014, 136, 17430. (3) a) Pietryga, J. M.; Werder, D. J.; Williams, D. J.; Casson, J. L.; Schaller, R. D.; Klimov, V. I.; Hollingsworth, J. A. J. Am. Chem. Soc. 2008, 130, 4879; b) Ha, D.-H.; Caldwell, A. H.; Ward, M. J.; Honrao, S.; Mathew, K.; Hovden, R.; Koker, M. K. A.; Muller, D. A.; Hennig, R. G.; Robinson, R. D. Nano Lett. 2014, 14, 7090; c) Lin, Q.; Makarov, N. S.; Koh, W.-k.; Velizhanin, K. A.; Cirloganu, C. M.; Luo, H.; Klimov, V. I.; Pietryga, J. M. ACS Nano 2015, 9, 539; d) Wang, X.; Liu, X.; Zhu, D.; Swihart, M. T. Nanoscale 2014, 6, 8852; e) Groeneveld, E.; Witteman, L.; Lefferts, M.; Ke, X.; Bals, S.; Van Tendeloo, G.; de Mello Donega, C. ACS Nano 2013, 7, 7913; f) Justo, Y.; Sagar, L. K.; Flamee, S.; Zhao, Q.; Vantomme, A.; Hens, Z. ACS Nano 2014, 8, 7948; g) De Trizio, L.; Li, H.; Casu, A.; Genovese, A.; Sathya, A.; Messina, G. C.; Manna, L. J. Am. Chem. Soc. 2014, 136, 16277. (4) a) Sahu, A.; Kang, M. S.; Kompch, A.; Notthoff, C.; Wills, A. W.; Deng, D.; Winterer, M.; Frisbie, C. D.; Norris, D. J. Nano Lett. 2012, 12, 2587; b) Ott, F. D.; Spiegel, L. L.; Norris, D. J.; Erwin, S. C. Phys.Rev. Lett. 2014, 113, 156803. (5) Routzahn, A. L.; Jain, P. K. Nano Lett. 2014, 14, 987. (6) Potter, R. W. Econ. Geol. 1977, 72, 1524. (7) a) Li, H.; Zanella, M.; Genovese, A.; Povia, M.; Falqui, A.; Giannini, C.; Manna, L. Nano Lett. 2011, 11, 4964; b) Jain, P. K.; Amirav, L.; Aloni, S.; Alivisatos, A. P. J. Am. Chem. Soc. 2010, 132, 9997. (8) a) Qu, Z.; Yan, L.; Li, L.; Xu, J.; Liu, M.; Li, Z.; Yan, N. ACS Appl. Mater. Interf. 2014, 6, 18026; b) Wang, H.; Lou, S.; Tang, Z.; Xu, W.; Shang, H.; Shen, H.; Li, L. S. Dalton Trans. 2012, 41, 12726; c) Miszta, K.; Brescia, R.; Prato, M.; Bertoni, G.; Marras, S.; Xie, Y.; Ghosh, S.; Kim, M. R.; Manna, L. J. Am. Chem. Soc. 2014, 136, 9061. (9) Haynes, W. M.; Lide, D. R. CRC Handbook of Chemistry and Physics; CRC Press: Boca Raton, Fla., 2011. (10) Moon, G. D.; Ko, S.; Xia, Y.; Jeong, U. ACS Nano 2010, 4, 2307. (11) Luo, Y.-R. Comprehensive handbook of chemical bond energies; CRC Press: Boca Raton, FL :, 2007. (12) Dean, J. A.; Lange, N. A. Lange's Handbook of Chemistry; McGraw-Hill, 1999. (13) a) Bouet, C.; Laufer, D.; Mahler, B.; Nadal, B.; Heuclin, H.; Pedetti, S.; Patriarche, G.; Dubertret, B. Chem. Mater. 2014, 26, 3002; b) Adel, P.; Wolf, A.; Kodanek, T.; Dorfs, D. Chem. Mater. 2014, 26, 3121.

Corresponding Author [email protected], [email protected]

Author Contributions K. M., G. G. and R. B. contributed equally to this work.

ACKNOWLEDGMENT

ACS Paragon Plus Environment

Page 5 of 5

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Journal of the American Chemical Society

Insert Table of Contents artwork here

ACS Paragon Plus Environment